Plastic Mould Steel Suppliers in Mumbai
P-20 Tool Steel
Plastic Mould Steel Suppliers in Mumbai is characterized by strong dimensional heating stability, good polishability, high-intensity resistance, and good wear properties. Various levels can offer much better polishability or enhanced dimensional stability within the general category of mould steel. Some even offer enhanced resistance to corrosion which makes them extremely appropriate for chemical assertive plastics moulding. Many mould steels are delivered pre-hardened.
The selection of the appropriate mould material based on the characteristics of plastic material of been moulded, manufacturing process, amount of sections to be created, specifications, and surface finishing. Suman Steel offers outstanding product advice and guidance across all sectors, from over numerous years of rich experience throughout the steel industry. Plastic Mould Steel Supplier is normally used within pre hardend situation that allows the consumer to utilizes the steel immediately only by die cutting it. The specific advantages of this steel specimen are that, after cutting tools, it protects strengthening. This can be used along with specific supplied situation with very broad measurements. The demands of the end product are determined also by the stress of plastic mould as well as the demands upon the grade of steel needed. The moulds being used while processing plastics are quite disparate in their usability as well as the demands placed on them. The right solution and treatment of the grade of steel influences firmly the performance and leading profit margins of plastic manufactured. We concentrate on a professionally trained team of experts in the steels for a plastic moulding way to ensure that the expectations of the customer are fulfilled. They form a perfectly executed team along with the mould manufacturers to evaluate which steel grade and efficiency are best suited to the independent profile requirements as described by the end plastic product. We are interested in providing a large variety of products to satisfy specific customer requirements. Being such a best-known organization, we are committed to offering a respected line of products. In the construction sector, we have highlighted the increasing necessity of steel plates and profiles. The selection of Plastic Mould Steel Suppliers in Mumbai relies on the total life span of the mould, component surface quality, and plastic materials. The greater the mould overall existence, the greater demand for strength properties and plastic mould steel Supplier toughness should be required. Suman Steel represents a significant example of steady business development. Today all over the Market, the steel constructing and casting industrial sector completely understands our organizational and business abilities. We also support our customers to provide them with all sorts of information necessary by linking up for this reason with large corporations & contractors.
Chemical composition:
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
|
1.2311 |
0.35-0.45 |
0.20-0.40 |
1.3O-1.60 |
1.8-2.10 |
0.15-0.25 |
- |
≤ 0.035% |
≤ 0.035% |
|
1.2312 |
0.35-0.45 |
0.30-0.50 |
1.4O-1.60 |
1.8-2.10 |
0.15-0.25 |
≤ 0.035% |
≤ 0.035% |
|
|
1.2738 |
0.35-0.45 |
0.20-0.40 |
1.3O-1.60 |
1.8-2.10 |
0.15-0.25 |
0.9-1.2 |
≤ 0.03% |
≤ 0.03% |
|
1.2316 |
0.33-0.43 |
1.00% MAX |
1.50% MAX |
15.5-17.5 |
0.8O-1.30 |
≤ 1.00% |
≤ 0.03% |
≤ 0.03% |
|
1.2083 |
0.36-0.46 |
1.00% MAX |
1.00% MAX |
12.5-14.5 |
≤ 0.03% |
≤ 0.03% |
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2311 |
VP20ISOF |
M202 |
618 |
ISO-BM |
1.2311 |
1.2311 |
UTOPNEX |
KEYLOS2311 |
- |
HPM7 |
KPM30 |
PCM40 |
HP4A |
GMP20[ESR] |
GS3D |
YTJ20A |
P-20 |
|
|
1.2312 |
VP20ISOFS |
- |
HOLDAX |
- |
1.2312 |
- |
UTOP N |
KEYLOS2312 |
- |
- |
- |
PCM40S |
- |
GS3S |
- |
P-20+Su |
||
|
1.2738 |
VP20ISO |
M238 |
IMPAX SUPREME |
ISO-BM |
1.2738 |
1.2738 |
UTOPNIN |
KEYLOS2738 |
- |
HPM |
- |
- |
- |
GMP20+Ni [ESR] |
LDHN |
YTJ21 |
P-20Ni |
|
|
1.2316 |
- |
M300 |
RAMAX S |
ISO-B |
1.2316 |
1.2316 |
PK335 |
KEYLOS2316 |
UPS3 |
HPM77 |
- |
- |
- |
1.2316 [ESR] |
- |
YTG173 |
420 |
|
|
1.2085 |
- |
- |
- |
- |
1.2085 |
- |
- |
- |
- |
- |
- |
- |
- |
- |
- |
420 |
||
|
1.2083 |
VP420IM |
M310 |
STAVAX |
ISO-B |
1.2083 |
1.2083 VICTORY |
PK4EX |
KEYLOS2083 |
- |
S-STAR |
HPM38 |
- |
SUS420J2 |
HEMS1A |
GMP420 [ESR] |
AK4R |
YTG136 |
420 |
1.2311
Equivalent grades:
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2311 |
VP20ISOF |
M202 |
618 |
ISO-BM |
1.2311 |
1.2311 |
UTOPNEX |
KEYLOS2311 |
- |
HPM7 |
KPM30 |
PCM40 |
HP4A |
GMP20[ESR] |
GS3D |
YTJ20A |
P-20 |
|
Alloyed and pre-toughened tool steel, especially suitable for polishing; high dimensional stability.
1.2311 ROUND BAR |
1.2311 FLAT BAR |
1.2311 SQUARE
|
1.2311 PLATE / SHEETS |
1.2311 FORGED BARS
|
1.2311 ROLLED BARS
|
1.2311 PEELED or 1.2311 BRIGHT
|
Application:
Moulding plates, inserts and high-tensile machine parts
Chemical Composition:
|
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
1.2311 |
0.35-0.45 |
0.20-0.40 |
1.3O-1.60 |
1.8-2.10 |
0.15-0.25 |
- |
≤0.035% |
≤0.035% |
|
Annealing |
710 - 730°C |
||||||||||
|
Hardness after annealing |
Max. 230 HB |
||||||||||
|
Stress relieving |
Approx 650°C |
||||||||||
|
Hot forming |
1050 - 850°C |
||||||||||
|
Hardening |
870 - 890°C |
||||||||||
|
Quenching media |
Oil, Salt bath,vacuum |
||||||||||
|
Hardness after quenching |
50 - 54 HRC |
||||||||||
|
Hardness after tempering :
|
|
1.2312
Equivalent grades:
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2312 |
VP20ISOFS |
- |
HOLDAX |
- |
1.2312 |
- |
UTOP N |
KEYLOS2312 |
- |
- |
- |
PCM40S |
- |
|
GS3S |
- |
P-20+Su |
|
Alloyed and pre-toughened tool steel acquires the property of excellent machinability in the hardened condition because of the Sulphur additive. It thus results into high dimensional stability. Compared to 1.2311 grade in 1.2312, 30% increase in milling speed and 300% increase in drilling speed can be expected. But 1.2312 is not suitable for polishing requirements.
Plastic injection mould cores and cavities, extursion dies for thermoplastics (PE, PP, PS), thermosetting plastics, transparent melts.
| 1.2312 ROUND BAR |
1.2312 FLAT BAR |
1.2312 SQUARE
|
1.2312 PLATE / SHEETS |
1.2312 FORGED BARS
|
1.2312 ROLLED BARS
|
1.2312 PEELED or 1.2311 BRIGHT
|
Application:
Plates for mould tools and dies with increased requirements on strength; high-tensile machine parts
Chemical composition:
|
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
1.2312 |
0.35-0.45 |
0.30-0.50 |
1.4O-1.60 |
1.8-2.10 |
0.15-0.25 |
|
≤0.035% |
≤0.035% |
Heat Treatment:
|
Annealing |
710 - 730°C |
||||||||||
|
Hardness after annealing |
Max. 230 HB |
||||||||||
|
Stress relieving |
Approx 650°C |
||||||||||
|
Hot forming |
1050 - 850°C |
||||||||||
|
Hardening |
870 - 890°C |
||||||||||
|
Quenching media |
Oil, Salt bath,vacuum |
||||||||||
|
Hardness after quenching |
50 - 54 HRC |
||||||||||
|
Hardness after tempering :
|
|
1.2316
Equivalent grades:
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2316 |
- |
M300 |
RAMAX S |
ISO-B |
1.2316 |
1.2316 |
PK335 |
KEYLOS2316 |
UPS3 |
HPM77 |
- |
- |
- |
1.2316 [ESR] |
- |
YTG173 |
420 |
|
Corrosion resistant, high-alloy, polishable, pre-toughened tool stee
| 1.2316 ROUND BAR |
1.2316 FLAT BAR |
1.2316 SQUARE
|
1.2316 PLATE / SHEETS |
1.2316 FORGED BARS
|
1.2316 ROLLED BARS
|
1.2316 PEELED or 1.2311 BRIGHT
|
Application:
Moulds for processing corrosive plastics.
Chemical Composition:
|
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
1.2316 |
0.33-0.43 |
1.00% MAX |
1.50% MAX |
15.5-17.5 |
0.8O-1.30 |
≤1.00% |
≤0.03% |
≤0.03% |
Heat Treatment:
|
Annealing |
810 - 830°C |
||||||||||
|
Hardness after annealing |
Max. 235 HB |
||||||||||
|
Stress relieving |
Approx 650°C |
||||||||||
|
Hot forming |
1050 - 850°C |
||||||||||
|
Hardening |
1020 - 1040°C |
||||||||||
|
Quenching media |
Oil, Salt bath,vacuum |
||||||||||
|
Hardness after quenching |
48 - 52 HRC |
||||||||||
|
Hardness after tempering :
|
|
1.2378
Equivalent grades:
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2738 |
VP20ISO |
M238 |
IMPAX SUPREME |
ISO-BM |
1.2738 |
1.2738 |
UTOPNIN |
KEYLOS2738 |
- |
HPM |
- |
- |
- |
GMP20+Ni [ESR] |
LDHN |
YTJ21 |
P-20Ni |
|
Low-sulphur tool steel is supplied in pre-toughened condition. Due to its nickel content, it features uniform strength even with maximum plate dimensions.
| 1.2378 ROUND BAR |
1.2378 FLAT BAR |
1.2378 SQUARE
|
1.2378 PLATE / SHEETS |
1.2378 FORGED BARS
|
1.2378 ROLLED BARS
|
1.2378 PEELED or 1.2311 BRIGHT
|
Application:
Large cavity plates with deep cavities for items such as bumpers, dashboards, moulding frames.
Chemical composition:
|
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
1.2738 |
0.35-0.45 |
0.20-0.40 |
1.3O-1.60 |
1.8-2.10 |
0.15-0.25 |
0.9-1.2 |
≤0.03% |
≤0.03% |
Heat Treatment:
|
Annealing |
710 - 730°C |
||||||||||
|
Hardness after annealing |
Max. 240 HB |
||||||||||
|
Stress relieving |
Approx 650°C |
||||||||||
|
Hot forming |
1050 - 850°C |
||||||||||
|
Hardening |
870 - 890°C |
||||||||||
|
Quenching media |
Oil, Salt bath,vacuum |
||||||||||
|
Hardness after quenching |
50 - 54 HRC |
||||||||||
|
Hardness after tempering :
|
|
1.2083
Equivalent grades:
|
STANDARD |
BRAZIL |
AUSTRIA |
SWEDEN |
GERMANY |
SLOVANIA |
ITALY |
JAPAN |
S.KOREA |
TAIWAN |
CHEZ. |
CHINA |
AMERICAN |
||||||
|
MOULD |
VILLARES |
BOHLER |
AASAB |
BUDERUS |
DEW |
GRODITZ |
RAVNE |
LUCCHINI |
VARONA |
DAIDO |
HITACHI |
NIPPON |
SANYO |
DOOSAN |
GLORIA |
POLDI |
EST |
AISI |
|
1.2083 |
VP420IM |
M310 |
STAVAX |
ISO-B |
1.2083 |
1.2083 VICTORY |
PK4EX |
KEYLOS2083 |
- |
S-STAR |
HPM38 |
- |
SUS420J2 |
HEMS1A |
GMP420 [ESR] |
AK4R |
YTG136 |
420 |
Properties like Low corrosion, high-alloy, low warpage steel for through hardening with excellent properties for mirror polishing as well as good photoetching, good machinability, high wear resistance and high dimensional stability is expected from this steel.
<| 1.2083 ROUND BAR |
1.2083 FLAT BAR |
1.2083 SQUARE
|
1.2083 PLATE / SHEETS |
1.2083 FORGED BARS
|
1.2083 ROLLED BARS
|
1.2083 PEELED or 1.2311 BRIGHT
|
Application:
Mould plates and inserts for working with chemically aggressive plastics; because of excellent polishing, suitable for optical and medical products
Chemical Composition:
|
|
CARBON C % |
SILICON Si% |
MANGANESE Mn% |
CHROMIUM Cr% |
MOLYBDENUM Mo% |
NICKEL Ni% |
SULPHUR |
PHOSPHORUS P% |
|
1.2083 |
0.36-0.46 |
1.00% MAX |
1.00% MAX |
12.5-14.5 |
|
|
≤0.03% |
≤0.03% |
Heat Treatment:
|
Annealing |
810 - 830°C |
||||||||||
|
Hardness after annealing |
Max. 230 HB |
||||||||||
|
Stress relieving |
Approx 650°C |
||||||||||
|
Hot forming |
1050 - 850°C |
||||||||||
|
Hardening |
870 - 990°C |
||||||||||
|
Quenching media |
Oil, Salt bath,vacuum |
||||||||||
|
Hardness after quenching |
52 - 56 HRC |
||||||||||
|
Hardness after tempering :
|
|
|
Steel Classification |
Standard |
|
Assab |
Bohler |
Edelstahl |
Thyssen |
Hitachi |
||
|
DIN |
JIS |
AISI |
|||||||
|
Plastic Mould Steel |
1.1203 |
SUS 420 J2 |
1055 |
|
- |
- |
- |
CK 55 |
SCS 2 |
|
1.2311 |
P20 |
|
718 |
W330 |
2311 iso BM |
2311 |
|||
|
1.2312 |
P20+S |
|
Holdax |
M200 |
2312 |
2312 |
|||
|
1.2738 |
P20+Ni |
|
Impax |
- |
- |
2738 |
|||
|
1.2316 |
- |
|
RaMaxS |
M300 |
- |
2316 |
|||
|
1.2083 |
420 |
|
Stavax |
M310 |
2083 |
2083 |
|||
|
1.2085 |
420+S |
|
- |
M304 |
21 MnCr 5 |
- |
|||
|
1.2162 |
- |
|
Prexi |
M100 |
- |
2162 |
|||
|
|
|||||||||
|
Hot Work Steel |
1.2344 |
SKD 61 |
H13 |
|
8407 |
W302 |
2344 ISO B |
2344 |
DAC |
|
1.2714 |
SKT 4 |
L6 |
|
SOMDIE |
W500 |
2714 |
2714 |
DM |
|
|
1.2367 |
- |
- |
|
QRO90 |
W303 |
2367 ISO B |
2367 |
- |
|
|
1.2767 |
- |
- |
|
Grane |
K600 |
X45CrNiMo4 |
- |
- |
|
|
|
|||||||||
|
Cold Work Steel |
1.1545 |
SK 4 |
W110 |
|
UHB20 |
K990 |
C105W1 |
1545 |
SK4 |
|
1.2436 |
- |
- |
|
Sverker 3 |
K107 |
X210CrW12 |
2436 |
- |
|
|
1.2510 |
SKS 3 |
O-1 |
|
DF2 |
K460 |
2510 |
2510 |
SGT |
|
|
1.2363 |
SKD 12 |
A2 |
|
XW40 |
K305 |
2363 |
2363 |
SCD |
|
|
1.2379 |
SKD 11 |
D2 |
|
XW41 |
K110 |
2379 ISO B |
2379 |
SLD2 |
|
|
1.2550 |
SKS 41 |
S1 |
|
M4 |
K455 |
2550 |
2550 |
- |
|
|
1.2842 |
- |
O-2 |
|
Aros |
K720 |
90MnCrV3 |
2842 |
- |
|